ABS-Like OdorLite Resin
Product Overview
ABS-Like OdorLite Resin offers excellent toughness, capable of resisting 19J/m impact and 180-degree bending without cracking. A specialized vacuum deodorization process reduces odor by up to 90%, significantly improving the working environment.
Material Status
| Characteristics | Toughness, Impact resistance, Low smell |
| Applications | Miniature model, Prototype design |
| Appearance | Multiple Colors |
| Form | Resin |
| Processing method | (surface exposure molding) LCD, (surface exposure molding) DLP |
Physical Properties
| Property | Testing Method | Typical Value |
|---|---|---|
| Density | ASTM D792 | 1.05-1.25 g/cm³ |
| Viscosity | ASTM D445 | 300-600 mPa·s |
| Hardness | ASTM D2240 | 80-84 ShoreD |
Mechanical Properties
| Property | Testing Method | Typical Value | Unit |
|---|---|---|---|
| Tensile Strength | ASTMD638 | 47.3 | MPa |
| Elongation at Break | ASTMD638 | 8.99 | % |
| Flexural Strength | ASTMD790 | 64 | MPa |
| Izod Notch Impact Strength | ASTMD638 | 20 | J/m |
| Thermal Deformation Temperature@0.45MPa | ASTMD648 | 63.75 | °C |
Note: The parameters above are for reference only. The performance of cured materials can be influenced by factors such as equipment, environment, parameter settings, post-processing methods, and testing methods, which may lead to significant variations. Please contact eSUN for further assistance if needed.
Testing Specimen Descriptions
- Tensile testing specimen: ASTM D638
- Flexural testing specimen: ASTM D790
- IZOD Impact Strength specimen: ASTM D638
Print Parameters
| Representative Machine | Exposure Time/s | Bottom Exposure Time/s | Bottom Layer Count | Lift Distance/mm | Lift Speed /mm·min⁻¹ | Retract Speed /mm·min⁻¹ |
|---|---|---|---|---|---|---|
| ELEGOO Saturn 3U | 2.5 | 25 | 5 | 7 | 90 | 240 |
| ELEGOO Saturn 4U 12K | 2.5 | 25 | 5 | 8 | 120 | 240 |
| ANYCUBIC Photon Mono M7 | 2.5 | 25 | 5 | 8 | 120 | 240 |
| ANYCUBIC Photon Mono M7P | 2.5 | 25 | 5 | 8 | 120 | 240 |
| ANYCUBIC Photon Mono M7M | 2.5 | 25 | 5 | 8 | 120 | 240 |
| AnyCubic Mono 4Ultra | 2 | 20 | 5 | 6 | 120 | 240 |
| NOVA3D Whale 4 | 2 | 25 | 5 | 8 | 120 | 240 |
| UniFormation GK 3 | 2 | 25 | 5 | 7 | 100 | 360 |
| CREALITY HALOT MAGE Pro | 1.2 | 30 | 5 | 8 | 240 | - |
| CREALITY HALOT MAGE S | 2.5 | 25 | 5 | 8 | 240 | - |
| PHROZEN Sonic Mighty 14K | 2.5 | 25 | 5 | 8 | 60 | 150 |
| PHROZEN Sonic Mighty 8K | 2.5 | 25 | 5 | 8 | 60 | 150 |
| PHROZEN Sonic Mighty 8KS | 2.5 | 20 | 5 | 8 | 40 | 180 |
Post-Curing Treatment
It is recommended to use a 36W 405nm UV curing chamber for 5-10 minutes as standard practice. For performance testing, cure mechanical test specimens on both sides separately for 30 minutes per side to ensure performance stability.
Matters Needing Attention
- Shake well before use. Wear gloves and a mask when using.
- Store in a sealed container at an ambient temperature of 20-35°C, avoiding direct sunlight.
- This product is not for consumption. Keep away from children and pregnant women.
- After printing, the model should be cleaned with 95% alcohol (unless it is a water-washable resin) to make the surface non-sticky.
Notice
All information supplied by or on behalf of eSUN in relation to this product, whether in the nature of data, recommendations or otherwise, is supported by research and believed to be reliable in good faith. However, the product is sold "as is". eSUN assumes no liability and makes no representations or warranties, express or implied, of merchantability, fitness for a particular purpose, or of any other nature with respect to the information or the product to which the information refers. Nothing herein waives any of the seller's conditions of sale.